Thermal Degradation And Stabilization Of PVC
Polyvinyl chloride is used as a third-most widely produced plastic formed by the polymerization of vinyl chloride and has tremendous applications all around. It is thermally degraded by dehydro- chlorination, in the absence of oxygen and evolves HCl. Thermogravimetry (TG/DTG) coupled with evolved gas analysis (MS detection) of volatiles was used to characterize the thermal behavior of commercial PVC cable insulation material during heating in the range 20-800°C in air and nitrogen, respectively. In addition, simultaneous TG/FTIR was used to elucidate chemical processes that caused the thermal degradation of the sample. There are two general approaches to the stabilization of polymers by modification of molecular structure and the use of additives. This degradation must be controlled by the addition of stabilizers. The mainly used stabilizers are Schiff bases, Alkyltin Stabilizers, Mixed Metal Stabilizers, Alkyl Phosphites Stabilizers, ? -Diketones Stabilizers, Epoxidized Fatty Acid Esters Stabilizers, Hydrotalcites Stabilizers, Tin Stabilizers, Organotin Mercaptides and Organotin Sulfide Organotin Carboxylates. The heat stabilizer must prevent the dehydrochlorination reaction. Among these Schiff bases were find best regarding environmental effects.
1.0 Introduction
1.1 Background to the Study
Poly (vinyl chloride) is commonly abbreviated as PVC, It is the third-most widely pro- duced plastic,after polyethylene and polypropylene.[1] PVC is used in construction because it is more effective than traditional materials such as copper, iron or wood in pipe and profile ap- plications. It can be made softer and more flexible by the addition of plasticizers, the most widely used being phthalates. In this form, it is also used in clothing and upholstery, electrical cable insulation, inflatable products and many ap- plications in which it replaces rubber. [2]
Pure polyvinyl chloride is a white, brittle solid. It is insoluble in alcohol, but slightly soluble in tetrahydrofuran. [3] PVC is useful because it resists two things that hate each other: fire and water. Because of its water resistance it’s used to make rain coats and shower curtains, and of course, water pipes. It has flame resistance, too, because it contains chlorine. When you try to burn PVC, chlorine atoms are released, and chlo- rine atoms inhibit combustion.
Structurally, PVC is a vinyl polymer. It’s similar to polyethylene, but on every other car- bon in the backbone chain, one of the hydrogen atoms is replaced with a chlorine atom. It’s pro- duced by the free radical polymerization of vinyl chloride. PVC can also be prepared by treating acetylene with hydrochloric acid (HCl). [5] (Figure 1)
Figure 1: Synthesis of poly (vinyl chloride)
Polyvinylchloride (PVC) is a plastic that is used in a variety of applications. For electrical wire coatings, the application of concern for this thesis, the PVC formulations typically include numerous additives. At a minimum the formulations include aplasticizer and thermal stabilizers. Plasticizers are utilized to increase the flexibility of the polymer. Thermal stabilizers are utilized to prevent degradation of the polymer backbone by either substitution of the stabilizer for labile chlorides or scavenging the HCl released from the degradation process.4 HCl released as part of the degradation process can catalyse further degradation by coordinating to labile chlorides and promoting their elimination from the backbone.
Phthalates such as diisodecyl phthalate (DIDP), bis(2-ethylhexyl) phthalate (DEHP), and diisononyl phthalate (DINP) are the most commonly utilized plasticizers for PVC formulations. In fact, they represent 85% of the global plasticizer consumption (6 Mton/year).5 However, phthalate plasticizers are derived entirely from crude oil, which is a nonrenewable fossil fuel whose costs are constantly increasing (Figure 1).6 Additionally, the leaching of low weight phthalate plasticizers such as DEHP from the polymer is facing increased scrutiny due to health concerns.7
1.2 Statement of Problem
Bio-based plasticizers derived from the oils of plants or from starch – such as castor, soybean, palm, grapeseed, sunflower and linseed – are being investigated as replacements for phthalate plasticizers. Plasticizers derived from plant oils contain double bonds which are often epoxidized to increase solubility in the PVC polymer.8-10 The use of bio-based stabilizers is hoped to introduce long-term sustainability to the PVC market due to the renewability of the feed-stock used for plasticizer production.
In order to maintain polymer performance after processing, thermal stabilizers such as metal soaps of stearates (ex. zinc stearate, calcium stearate) are also added to the PVC formulation.4-5 While the thermal degradation and stabilization of PVC in the presence of phthalate plasticizers has been studied, the research is largely segmented and focused on model studies in reaction solvents. This study details the integration of model studies and bulk PVC studies on the thermal degradation and stabilization of the polymer in the presence of stearate stabilizers and phthalate plasticizers. A comprehensive mechanism of the stabilization and degradation via zinc and calcium stearates is described.
1.3 Aims and Objectives
The aim of this study is to investigate thermal degradation and stabilization of PVC. The objectives are as follows;
- To identify the stages and processes of thermal degradation of PVC
- To characterize the thermal behavior of PVC
- To review the stabilization process and materials for PVC
The Title Page should be the first section of your project “Thermal Degradation And Stabilization Of PVC”, providing essential details like the project title, your name, your supervisor’s name, the institution, and the submission date. After that, the Abstract offers a brief summary of your project, touching on its purpose, methods, results, and conclusions in 150-300 words. The Acknowledgments section is where you can thank those who supported your research, such as your supervisor, peers, or organizations that provided resources.
Next, the Table of Contents organizes the Thermal Degradation And Stabilization Of PVC by listing its chapters and sections, along with page numbers for easy reference. The List of Figures and List of Tables help guide readers to specific visual elements like graphs, charts, or tables included in the document. There should also be an Abbreviations and Glossary section to explain any specialized terms or acronyms, making the content clearer to readers unfamiliar with the technical language.
The main body of the Thermal Degradation And Stabilization Of PVC should start with the Introduction, which provides background information, outlines the research problem, states your objectives, and gives a brief overview of your research methods. Following that, the Literature Review offers an in-depth look at previous research relevant to your project, identifying gaps your study aims to address. The Methodology section then explains the research design, tools, and data collection methods you used to conduct the project and analyze the data.
In the Results and Discussion section, you present your findings and discuss them in relation to the Thermal Degradation And Stabilization Of PVC research questions or objectives, often using tables or charts to help explain the data. The Conclusion summarizes the key results, discusses their implications, and suggests possible directions for future research. You may also include recommendations based on your findings, offering practical advice for improvements or applications. Finally, the Thermal Degradation And Stabilization Of PVC project should include a References or Bibliography section to list all the sources you cited, as well as Appendices for any additional material. A Statement of Originality is often included to confirm the authenticity of your work